| 60Si2CrVA弹簧断裂原因分析 |
| |
| 引用本文： | 侯珍,宫心勇,郑秋越.60Si2CrVA弹簧断裂原因分析[J].理化检验(物理分册),2013(11):777-780. |
| |
| 作者姓名： | 侯珍 宫心勇 郑秋越 |
| |
| 作者单位： | 天津机辆轨道交通装备有限责任公司,天津300232 |
| |
| 摘 要： | 通过断口分析、金相检验、硬度测试及化学成分分析等方法，对60Si2CrVA弹簧进行断裂原因分析。结果表明：该弹簧断裂失效性质为疲劳断裂；弹簧端圈磨削裂纹是导致弹簧断裂的根本原因；提出了防止磨削裂纹产生的建议．对指导生产有一定参考价值。
|
| 关 键 词： | 弹簧 疲劳断裂 磨削裂纹 |
Analysis on Fracture Reason of 60Si2CrVA Spring |
| |
| IIOU Zhen. GONG Xin-yong. ZHENG Qiu-yue.Analysis on Fracture Reason of 60Si2CrVA Spring[J].Physical Testing and Chemical Analysis Part A:Physical Testing,2013(11):777-780. |
| |
| Authors: | IIOU Zhen GONG Xin-yong ZHENG Qiu-yue |
| |
| Affiliation: | IIOU Zhen. GONG Xin-yong. ZHENG Qiu-yue( Tianjing Railway Transport Equipment Co,. Ltd ,Tianjing300232. China) |
| |
| Abstract: | In order to analyze tile fracture reason of 60Si2CrVA spring, the analysis such as fracture appearanee, microstructure, hardness and chemical compositions were conducted. The results indicated that the fracture of spring was fatigue, it＇s prime reason was grinding cracks on the end of the springrests. The prevention measures of grinding cracks on springs, which exhibited the special value for guiding the production, have been proposed. |
| |
| Keywords: | spring fatigue fracture grinding cracks |