Austenitization during intercritical annealing of an Fe-C-Si-Mn dual-phase steel

Partial austenitization during the intercritical annealing of an Fe-2.2 pct Si-1.8 pct Mn-0.04 pct C steel has been investigated on four kinds of starting microstructures. It has been found that austenite formation during the annealing can be interpreted in terms of a carbon diffusion-limited growth process. The preferential growth of austenite along the ferrite grain boundaries was explained by the rapid carbon supply from the dissolving carbide particles to the growing fronts of austenite particles along the newly formed austenite grain boundaries on the prior ferrite grain boundaries. The preferential austenitization along the grain boundaries proceeded rapidly, but the austenite growth became slowed down after the ferrite grain boundaries were site-saturated with austenite particles. When the ferrite grain boundaries were site-saturated with austenite particles in a coarse-grained structure, the austenite particles grew by the mode of Widmanstätten side plate rather than by the normal growth mode of planar interface displacement.