In situ polymerization monitoring of a diacrylate in an electrically conducting mesoporous nanoparticle scaffold |
|
| Authors: | Hoffmann Ron Naatz Hendrik Hartwig Andreas |
| Affiliation: | 1.Fraunhofer Institute for Manufacturing Technology and Advanced Materials (IFAM), Wiener Str. 12, 28359, Bremen, Germany ;2.Department 2 Biology/Chemistry, University of Bremen, Leobener Str. 3, 28359, Bremen, Germany ;3.Leibniz Institute for Materials Engineering IWT, Badgasteiner Str. 3, 28359, Bremen, Germany ;4.Faculty of Production Engineering, University of Bremen, Badgasteiner Str. 1, 28359, Bremen, Germany ; |
| Abstract: | The properties of nanoparticle–polymer composites strongly depend on the network structure of the polymer matrix. By introducing nanoparticles into a monomer (solution) and subsequently polymerizing it, the formation of the polymer phase influences the mechanical and physicochemical properties of the composite. In this study, semi-conducting indium tin oxide (ITO) nanoparticles were prepared to form a rigid nanoparticle scaffold in which 1,6-hexanediol diacrylate (HDDA), together with an initiator for photo-polymerization, was infiltrated and subsequently polymerized by UV light. During this process, the polymerization reaction was characterized using rapid scan Kubelka–Munk FT-IR spectroscopy and compared to bulk HDDA. The conductivity change of the ITO nanoparticles was monitored and correlated with the polymerization process. It was revealed that the reaction rates of the radical initiation and chain propagation are reduced when cured inside the voids of the nanoparticle scaffold. The degree of conversion is lower for HDDA infiltrated into the mesoporous ITO nanoparticle scaffold compared to purely bulk-polymerized HDDA. Graphical abstract |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ | |