The corrosion behaviour of Zr-based bulk metallic glasses in 0.5 M NaCl solution

The corrosion behaviour of eutectic Zr₅₀Cu₄₀Al₁₀ and hypoeutectic Zr₇₀Cu₆Al₈Ni₁₆ bulk metallic glasses (BMGs) was studied by electrochemical measurements, scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS). Zr₅₀Cu₄₀Al₁₀ BMG was highly susceptible to pitting corrosion in naturally aerated 0.5 M NaCl solution at 30 °C. In contrast, Zr₇₀Cu₆Al₈Ni₁₆ BMG passivated spontaneously under the same condition. EDX results for Zr₅₀Cu₄₀Al₁₀ indicated that enrichment of Cu, Cl and O occurred in the pitted region, while for Zr₇₀Cu₆Al₈Ni₁₆ BMG, no significant difference was found in the surface composition from the specimens before and after immersion in the solution. XPS analysis including angle-resolved measurements for Zr₇₀Cu₆Al₈Ni₁₆ BMG revealed that zirconium cation (Zr⁴⁺) was highly concentrated in both air-formed and passive films. Furthermore, the concentration of Zr⁴⁺ ions after immersion for 24 h or more showed tendency to increase with decreasing take-off angle, indicating that the exterior part of the passive film consisted exclusively of zirconium oxyhydroxide. The high corrosion resistance of Zr₇₀Cu₆Al₈Ni₁₆ BMG was attributed to the formation of homogeneous and stable passive film enriched with zirconium.