The fracture toughness measured on sensitized 304 stainless steel in simulated reactor water

The environmental conditions chemically equivalent to BWR primary water, e.g. 288°C, 0.2 ppm O₂ and/or 98°C, air-saturated, were found to influence considerably the in-water fracture toughness values of furnace-sensitized Type 304 stainless steel.Notched compact tension and three point bend specimens sampled from two heats of standard materials (0.06% C) showed significant reduction in dJ/da values reflecting consistently the effects of loading rate, temperature, dissolved oxygen concentration and degree of sensitization. In particular the crack enhancement with lowering the loading rate was significant. The effect became apparent with dJ dt at and below 1× 10−1 kg·mm/mm²/min (1.6 × 10 J/m²/s) in the typical BWR environment.Based on the results, it is suggested that a critical consideration is needed on the significance of such an environmental effect in the LWR structural safety evaluation, in particular that the probability of instable fracture at the “rings” of sensitized material near welded joints is subject to reviewing.