| 略钢铸坯夹杂缺陷成因分析和实践 |
| |
| 引用本文： | 尚巍巍,王济良,袁守谦. 略钢铸坯夹杂缺陷成因分析和实践[J]. 甘肃冶金, 2007, 29(5): 7-11 |
| |
| 作者姓名： | 尚巍巍 王济良 袁守谦 |
| |
| 作者单位： | 略阳钢铁有限责任公司,陕西,略阳,724300;西安建筑科技大学,陕西,西安,710000 |
| |
| 摘 要： | 对略钢生产的钢筋和圆钢出现冷弯断裂和延伸率下降情况的成因进行分析,确定主要是由于铸坯中夹杂物过多。通过采取一系列技术措施,取得了较好的效果,产品合格率明显提高。
|
| 关 键 词： | 铸坯 夹杂 分析 措施 |
| 文章编号： | 1672-4461（2007）05-0007-05 |
| 修稿时间： | 2007-03-21 |
Reasons Analysis and Practice on Inclusions Defects of Continuous Casting Billets in Lueyangsteel |
| |
| SHANG Wei-wei,WANG Ji-liang,YUAN Shou-qian. Reasons Analysis and Practice on Inclusions Defects of Continuous Casting Billets in Lueyangsteel[J]. Gansu Metallurgy, 2007, 29(5): 7-11 |
| |
| Authors: | SHANG Wei-wei WANG Ji-liang YUAN Shou-qian |
| |
| Abstract: | This article analyses the quality defects of hot rolled ribbed and plain steel bar in lueyangsteel. The reasons of the defects are quantity of inclusions in steel too more. Good results have been achieved upon implementation of the appro- priate counter measures. |
| |
| Keywords: | continuous casting billet inclusions in steel analysis measures |