| 喷射成形高合金化材料沉积坯内部疏松成因分析与改善 |
| |
| 引用本文： | 张勇,张国庆,李周,袁华,许文勇,付书红,王涛.喷射成形高合金化材料沉积坯内部疏松成因分析与改善[J].中国材料科技与设备,2012(6):65-67,99. |
| |
| 作者姓名： | 张勇 张国庆 李周 袁华 许文勇 付书红 王涛 |
| |
| 作者单位： | 中航工业北京航空材料研究院先进高温结构材料重点实验室,北京100095 |
| |
| 基金项目： | 国家973计划项目（2011CB606303-3） |
| |
| 摘 要： | 本文主要研究了大尺寸喷射成形高合金化材料高温合金沉积坯内部疏松成因及其改善工艺。研究认为，高温合金沉积坯中最后凝固部位液相金属补缩不足和断裂应变低是产生疏松的必要条件，而沉积坯的局部收缩变形产生的热应力是造成疏松的重要原因。通过有限元计算，提出一种热控喷射成形工艺，并得到试验验证。该工艺有效减少了坯体内部的疏松等冶金缺陷，改善了沉积坯的质量。
|
| 关 键 词： | 喷射成形 沉积坯 计算 冶金缺陷，改善 |
Computer Analysis to Metallurgical Defect in Large--size High--alloy Material Deposit Prepared by Spray Forming |
| |
| Z HANG Yong,Z HANG Guo -- qing,L I Zhou,YUAN Hua,XU Wen-- yong,FU Shu-- hong,WANG Tao.Computer Analysis to Metallurgical Defect in Large--size High--alloy Material Deposit Prepared by Spray Forming[J].Chinese Materials Science Technology & Equipment,2012(6):65-67,99. |
| |
| Authors: | Z HANG Yong Z HANG Guo -- qing L I Zhou YUAN Hua XU Wen-- yong FU Shu-- hong WANG Tao |
| |
| Affiliation: | ( Science and technology Laboratory of Advanced High Temperature Structural Materials Beijing Institute of Aeronautical Materials AVIC, Beijing, 100095, China) |
| |
| Abstract: | The formation of hot tear in large--size spray forming superalloy deposit is analyzed in this paper. We found that the no-- sufficient feeding of liquid metal and the low fracture strain in semi-- solid layer are the prerequisite_ And the thermal stress engendered by cooling contract in local position in deposit is an important reason to engender hot cracking. With the help of Finite Element Method （FEM） calculation and experiment data, A ＂Thermal Controlling Spray Forming＂ （TCSF） is raised to e- liminate hot cracking appeared in large size billets according to control the distribution of heat in billet during spray deposition process. And we obtain large size deposit of superalloy which has tight microstructure using the process ultimately. |
| |
| Keywords: | Spray forming Deposit Calculation Metallurgical defect Improving |