| 纺丝工艺对水解聚丙烯腈/羟基磷灰石复合纤维强力的影响 |
| |
| 引用本文： | 王娜,王晓,郝军,杨启鹏,李淳.纺丝工艺对水解聚丙烯腈/羟基磷灰石复合纤维强力的影响[J].大连工业大学学报,2012,31(2):150-153. |
| |
| 作者姓名： | 王娜 王晓 郝军 杨启鹏 李淳 |
| |
| 作者单位： | 1. 大连工业大学纺织与材料工程学院,辽宁大连,116034
2. 大连工业大学轻工与化学工程学院,辽宁大连,116034 |
| |
| 基金项目： | 辽宁省教育厅重点实验室项目(2008S014);辽宁省自然科学基金项目(20082151);教育部留学归国人员启动基金项目(20091001) |
| |
| 摘 要： | 采用湿法纺丝法制备了水解聚丙烯腈/羟基磷灰石复合纤维,考察了凝固浴成分比例、凝固浴温度、凝固浴中碱浓度、冷牵伸比、热牵伸比及二浴水解时间等工艺因素对聚丙烯腈/羟基磷灰石复合纤维强力的影响。研究结果表明,水解聚丙烯腈/羟基磷灰石复合纤维具有可纺性,具有良好的强力。在NaOH水溶液/二甲基亚砜质量比为2∶8、NaOH水溶液浓度1mol/L、凝固温度10℃、喷丝头牵伸比1∶2、冷牵伸比1∶2、热牵伸比8倍和无二浴水解的条件下,所制备的水解聚丙烯腈/羟基磷灰石复合纤维具有很好的强力。
|
| 关 键 词： | 聚丙烯腈 羟基磷灰石 复合纤维 湿法纺丝 |
Effects of spinning parameters of hydrolyzed polyacrylonitrile/hydroxyapatite composite fiber on tensile strength |
| |
| WANG Na
,
WANG Xiao
,
HAO Jun
,
YANG Qi-peng
,
LI Chun.Effects of spinning parameters of hydrolyzed polyacrylonitrile/hydroxyapatite composite fiber on tensile strength[J].Journal of Dalian Dalian Polytechnic University,2012,31(2):150-153. |
| |
| Authors: | WANG Na WANG Xiao HAO Jun YANG Qi-peng LI Chun |
| |
| Affiliation: | 1.School of Textile and Material Engineering,Dalian Polytechnic University,Dalian 116034,China; 2.School of Light Industry and Chemical Engineering,Dalian Polytechnic University,Dalian 116034,China |
| |
| Abstract: | The hydrolyzed polyacrylonitrile/hydroxyapatite composite fiber was prepared via wet spinning.The effects of coagulation bath composition,coagulation temperature,NaOH concentration in coagulation bath,cold draw ratio,hot draw ratio and hydrolysis time in second coagulation bath on tensile strength of composite fibers were studied.Good strength of spinnable hydrolyzed polyacrylonitrile/hydroxyapatite composite fiber was obtained at the conditions of mass ratio of NaOH aqueous solution/DMSO of 2∶8,NaOH concentration of 1 mol/L,spinneret draw ratio of 1∶2,cold draw ratio of 1∶2,8 times drawing without hydrolysis in second coagulation bath. |
| |
| Keywords: | polyacrylonitrile hydroxyapatite composite fiber wet spinning |