Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li1/3Nb2/3)0.84Ti0.16]O3−δ Ceramics for LTCC Applications

The effects of LiF and ZnO–B₂O₃–SiO₂ (ZBS) glass combined additives on phase composition, microstructures, and microwave dielectric properties of Ca[(Li_1/3Nb_2/3)_0.84Ti_0.16]O_3−δ (CLNT) ceramics were investigated. The LiF and ZBS glass combined additives lowered the sintering temperature of CLNT ceramics effectively from 1150° to 880°C. The main diffraction peaks of all the specimens split due to the coexistence of the non-stoichiometric phase (A) and stoichiometric phase (B), which all possess CaTiO₃-type perovskite structures. The transformation from A into B became accelerated with the increase of LiF or ZBS content. ZBS glass restrained the volatilization of lithium salt, which greatly affected the microstructures and microwave dielectric properties. CLNT ceramics with 2 wt% LiF and 3 wt% ZBS sintered at 900°C for 2 h show excellent dielectric properties: ɛ_r=34.3, Q × f =17 400 GHz, and τ_f=−4.6 ppm/°C. It is compatible with Ag electrodes, which makes it a promising ceramic for low-temperature cofired ceramics technology application.