Decreasing miscibility with greater heterogeneity in ternary polymer blend: poly(cyclohexyl methacrylate), poly(α‐methyl styrene) and poly(4‐methyl styrene) |
| |
Authors: | Li Ling Chang E
M Woo |
| |
Affiliation: | Li Ling Chang,E M Woo |
| |
Abstract: | A ternary blend system comprising poly(cyclohexyl methacrylate) (PCHMA), poly(α‐methyl styrene) (PαMS) and poly(4‐methyl styrene) (P4MS) was investigated by thermal analysis, optical and scanning electron microscopy. Ternary phase behaviour was compared with the behaviour for the three constituent binary pairs. This study showed that the ternary blends of PCHMA/PαMS/P4MS in most compositions were miscible, with an apparent glass transition temperature (Tg) and distinct cloud‐point transitions, which were located at lower temperatures than their binary counterparts. However, in a closed‐loop range of compositions roughly near the centre of the triangular phase diagram, some ternary blends displayed phase separation with heterogeneity domains of about 1 µm. Therefore, it is properly concluded that ternary PCHMA/PαMS/P4M is partially miscible with a small closed‐loop immisciblity range, even though all the constituent binary pairs are fully miscible. Thermodynamic backgrounds leading to decreased miscibility and greater heterogeneity in a ternary polymer system in comparison with the binary counterparts are discussed. © 2003 Society of Chemical Industry |
| |
Keywords: | poly(cyclohexyl methacrylate) poly(α ‐methyl styrene) poly(4‐methyl styrene) DSC partial miscibility ternary blends |
|
|