Room temperature synthesis of Si-MCM-41 using polymeric version of ethyl silicate as a source of silica

Synthesis of mesoporous MCM-41 materials at room temperature using less expensive polymeric version of ethyl silicate (40 wt% SiO₂) as a source of silica was established. The influence of crucial synthesis parameters such as molar ratios of H₂O/NH₄OH, NH₄OH/SiO₂ and CTMABr/SiO₂ in gel on the quality of the phase formed was investigated. Powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and low temperature N₂ adsorption-desorption isotherms have been employed to characterize the products. The magnitude of orderness, textural properties and thermal stability of the Si-MCM-41 samples prepared under identical judiciously pre-controlled synthesis conditions using ethyl silicate and conventional tetraethyl orthosilicate (TEOS) were assessed. Even though, ethyl silicate has proved to be suitable source for the preparation of MCM-41 at room temperature, there exists an optimum value of H₂O/NH₄OH for different NH₄OH/SiO₂ molar ratios in the gel. Changes in the morphology were observed when NH₄OH/SiO₂, H₂O/NH₄OH molar ratios in the gels were changed.