Properties of TiO2 prepared by acid treatment of BaTiO3

TiO₃ powders were prepared by acid treatment of BaTiO₃ and their properties were investigated. The BaTiO₃ powder was subjected to HNO₃ in concentrations ranging from 10⁻³ to 8 M at 90 °C for 0.5-6 h. Dissolution of BaTiO₃ and precipitation of TiO₂ occurred at acid concentrations of 2-5 M. BaTiO₃ dissolves completely to form a clear solution at reaction times of 0.5-1 h, but a rutile precipitate is formed after 2 h of acid treatment. By contrast, anatase is precipitated by adjusting the pH of the clear solution to 2-3 using NaOH or NH₄OH solution. The rutile crystals were small and rod-shaped, consisting of many small coherent domains connected by grain boundaries with small inclination angles and edge dislocations, giving them a high specific surface area (S_BET). With increasing HNO₃ concentration, the S_BET value increased from 100 to 170 m²/g while the crystallite size decreased from 25 to 11 nm. The anatase crystals obtained here were very small equi-axial particles with a smaller crystallite size than the rutile and S_BET values of about 270 m²/g (higher than the rutile samples). The photocatalytic activity of these TiO₂ was determined from the decomposition rate of Methylene Blue under ultraviolet irradiation. Higher decomposition rates were obtained with larger crystallite sizes resulting from heat treatment. The maximum decomposition rates were obtained in samples heated at 500-600 °C. The photocatalytic activity of the TiO₂ was found to depend more strongly on the sample crystallite size than on S_BET.