Effects of the Weak Absorption Tail on the Transmission Loss of Ge–Sb–Se Optical Fibers

Selenide glass optical fibers were fabricated for Ge₃₀Sb₁₀Se₅₈S₂ and Ge₂₀Sb₁₀Se₇₀ glasses. Their transmission loss has been measured and compared with the theoretical attenuation loss that was calculated taking into account the electronic transition absorption, Rayleigh scattering, and multiphonon absorption. A low attenuation loss of the Ge₂₀Sb₁₀Se₇₀ glass composition in 1.2–1.7 μm range has been expected due to its high optical band gap energy compared with the Ge₃₀Sb₁₀Se₅₈S₂ glass. However, the measured attenuation loss of the Ge₃₀Sb₁₀Se₅₈S₂ glass fiber was ～13 dB/m at 1.5 μm while Ge₂₀Sb₁₀Se₇₀ glass showed ～82 dB/m. An enhanced weak absorption tail due to the localized states of the Ge₂₀Sb₁₀Se₇₀ glass was responsible for this behavior. Structural defects are related to the localized states and discussed for the present glass compositions.