| Tb2Fe17-xCrx化合物的结构与磁性 |
| |
| 引用本文： | 郝延明,周严,赵淼.Tb2Fe17-xCrx化合物的结构与磁性[J].功能材料,2005,36(7):1045-1047. |
| |
| 作者姓名： | 郝延明 周严 赵淼 |
| |
| 作者单位： | 天津师范大学,物理系,天津,300074 |
| |
| 基金项目： | 国家自然科学基金资助项目(50271022);教育部优秀青年教师计划资助项目(1999);天津市自然科学基金资助项目(043602011) |
| |
| 摘 要： | 通过X射线衍射及磁测量手段研究了Tb2Fe17-xCrx（x=0、0．5、1．0、1．5、2．0、3．0)化合物的结构与磁性。研究结果表明Tb2Fe17-xCrx化合物具有Th2Ni17型结构，随着Cr替代量x的增加，Tb2Fe17-xCrx化合物的单胞体积呈现非线性的减小，而晶胞参数a、c呈现复杂的变化。分析表明Tb2Fe17-xCrx化合物中存在着较强的磁一弹耦合效应。对磁性质的研究结果表明随着Cr替代量x的增加，Tb2Fe17-xCrx化合物的居里温度升高，在x=1．0时达到最大值，为539K，当Cr替代量x继续增加时，Tb2Fe17-xCrx化合物的居里温度下降。随着Cr替代量x的增加，Tb2Fe17-xCrx化合物的自发磁化强度急剧下降，分析表明在Tb2Fe17-xCrx化合物中，Cr的磁矩反平行于Fe的磁矩。
|
| 关 键 词： | Tb2Fe17-xCrx化合物 X射线衍射 居里温度 自发磁化强度 |
| 文章编号： | 1001-9731(2005)07-1045-03 |
| 修稿时间： | 2004年11月22 |
Structural and magnetic properties of Tb2Fe17-xCrx compound |
| |
| HAO Yan-Ming,ZHOU Yan,ZHAO Miao.Structural and magnetic properties of Tb2Fe17-xCrx compound[J].Journal of Functional Materials,2005,36(7):1045-1047. |
| |
| Authors: | HAO Yan-Ming ZHOU Yan ZHAO Miao |
| |
| Abstract: | The crystal structure and magnetic properties of Tb_2Fe_(17-x)Cr_x(x=0,0.5,1.0,1.5,2.0,3.0) compounds have been investigated by means of X-ray diffraction and magnetization measurements.These compounds have Th_2Ni_(17)-type structure.The unit-cell volumes decrease non-linear with increasing x,The unit-cell parameters a and c show complicatedly behavior with increasing x.This implies there was a strong magneto-elastic effect.The Curie temperature T_c of Tb_2Fe_(17-x)Cr_x compounds increase with increasing x first,then decrease with further increasing x,the maximum value of T_c was 539K for x=1.0. The spontaneous magnetization of these compounds shows decrease rapidly with the increase of x.This implies that the magnetic moment of Cr atom was antiparallel to the magnetic moment of Fe atom in Tb_2Fe_(17-x)Cr_x compounds. |
| |
| Keywords: | Tb_2Fe_(17-x)Cr_x compound X-ray diffraction Curie temperature spontaneous magnetization |