Effects of annealing conditions on the properties of tantalum oxide films on silicon substrates

The formation of a SiO₂ layer at the Ta₂O₅/Si interface is observed by annealing in dry O₂ or N₂ and the thickness of this layer increases with an increase in annealing temperature. Leakage current of thin (less than 40 nm thick) Ta₂O₅ films decreases as the annealing temperature increases when annealed in dry O₂ or N₂. The dielectric constant vs annealing temperature curve shows a maximum peak at 750 or 800° C resulting from the crystallization of Ta₂O₅. The effect is larger in thicker Ta₂O₅ films. But the dielectric constant decreases when annealed at higher temperature due to the formation and growth of a SiO₂ layer at the interface. The flat band voltage and gate voltage instability as a function of annealing temperature can be explained in terms of the growth of interfacial SiO₂. The electrical properties of Ta₂O₅ as a function of annealing conditions do not depend on the fabrication method of Ta₂O₅ but strongly depend on the thickness of Ta₂O₅ layer.