Starch–methylcellulose–whey protein film properties |
| |
Authors: | SeungRan Yoo John M Krochta |
| |
Affiliation: | Department of Food Science and Technology, University of California, 374 Old Davis Road, Davis, CA 95616, USA |
| |
Abstract: | Four % (wt/wt) aqueous solutions were prepared at corn starch:methylcellulose:whey protein isolate (CS:MC:WPI) ratios of 2:2:2, 1:2:3, 2:1:3, 2:2:0, 1:2:0 and 2:1:0. Glycerol (gly) was used as a plasticiser at CS–MC–WPI:gly ratios of 2:1, 2.5:1 and 3:1. CS–MC–WPI blend films were stronger than CS–WPI films and had lower oxygen permeability (OP) than MC–WPI films. The highest tensile strength (TS) of blend films was 8.01 ± 3.41 MPa, at CS:MC:WPI ratio of 2:2:0 and CS–MC–WPI:gly ratio of 3:1. Lowest OP value was 45.05 ± 7.24 cm3 μm m?2 per day kPa?1, at CS:MC:WPI ratio of 2:2:2 and CS–MC–WPI:gly ratio of 3:1. OP values were predictable based on relative amounts of components. However, TS and elastic modulus properties of the CS–MC–WPI blend films did not reflect the relative amounts of the components. All of CS–MC–WPI films were translucent indicating some degree of immiscibility among the CS, MC and WPI. These results indicate the influence of complex molecular interactions among the components. |
| |
Keywords: | Cellulose edible films starch whey protein |
|
|