| 低温锌系磷化液的研究 |
| |
| 引用本文： | 隋永强,梁成浩. 低温锌系磷化液的研究[J]. 表面技术, 2004, 33(5): 37-39 |
| |
| 作者姓名： | 隋永强 梁成浩 |
| |
| 作者单位： | 大连理工大学化工学院,辽宁,大连,116012;大连理工大学化工学院,辽宁,大连,116012 |
| |
| 摘 要： | 研制了一种新型低温锌系磷化液.通过耐蚀性、电化学测试及扫描电镜观察,表明碳钢经磷化后改善了阳极溶解性能,具有良好的耐蚀性能.磷化膜结晶组织呈网片状结构,均匀、密集,弥散分布,属结晶型磷化膜.该工艺成本低、成膜快、耐蚀性好、性能稳定,具有工业推广价值.
|
| 关 键 词： | 磷化 低温 耐蚀性 |
| 文章编号： | 1001-3660(2004)05-0037-03 |
Study on the Phosphating Solution of Zinc Series at Low Temperature |
| |
| SUI Yong-qiang,LIANG Cheng-hao. Study on the Phosphating Solution of Zinc Series at Low Temperature[J]. Surface Technology, 2004, 33(5): 37-39 |
| |
| Authors: | SUI Yong-qiang LIANG Cheng-hao |
| |
| Abstract: | A new type phosphating solution of zinc series at low temperature was prepared. Electrochemical test and scanning electron microscope method were investigated to analyse the phosphating film. The results indicated that the anodic dissolution performance of the carbon steel was improved after phosphating. According to the surface analysis, the phosphating film was crystal type, which appeared net and slices structure. Since this film was compact and uniform, it possessed good corrosion resistance. The phosphating process has advantages such as low cost, fast film-forming rate, stable performance and wide application value in industry. |
| |
| Keywords: | Phosphating Low temperature Corrosion resistance |