Structural, magnetic and magnetostrictive studies of Tb0.27Dy0.73(Fe1 − xAlx)2

Measurements of magnetic properties, X-ray diffraction and magnetostriction were made on Tb_0.27Dy_0.73(Fe_{1 − x}Al_x)₂ (x = 0.1, 0.2, …, 0.7) compounds. It was found that the system has the cubic MgCu₂ structure over almost the whole (Fe,Al) concentration range investigated, except for a narrow intermediate range (x = 0.4–0.6) where the hexagonal MgZn₂ structure appears. With increasing Al content x, the lattice constant a increases linearly with x. The first replacement of Fe results in a marked decrease in the Curie temperature, which is followed by a slight decrease in T_C with x. A linear decrease in magnetostriction of |λ_| − λ| at room temperature with x was also observed from 1530 × 10⁻⁶ for x=0 to 36×10⁻⁶ for x=0.3. The saturation magnetization σ_s exhibits a complex concentration dependence in the Tb_0.27Dy_0.73(Fe)_{1 − x}Al_x)₂ system: in the range x < 0.5, σ_s increases linearly with x and, for x = 0.5–0.6, σ_s decreases and then increases again. An enhancement of the magnetic ‘hardness’ in this system was also observed at low temperature.