Cathodic deposition and characterization of tin oxide coatings on graphite for electrochemical supercapacitors

Amorphous tin oxide (SnO_x) was cathodically deposited onto graphite electrode in a bath containing 0.1 M stannous chloride (SnCl₂), 0.5 M sodium nitrate (NaNO₃), and 0.4 M nitric acid (HNO₃) in an aqueous solution of 50% (v/v) ethanol. The SnO_x coatings grown on graphite were characterized as typical capacitive behaviors by cyclic voltammetry (CV), chronopotentiometric (CP) in 0.5 M KCl. Specific capacitance (in milli-farad per square centimeter, C_a) changes linearly with the deposition charge up to 4.5 C cm⁻², and a maximum of as high as 355 mF cm⁻² was obtained with the SnO_x coating grown at around 5 C cm⁻². For the SnO_x coating deposited at 0.2 C cm⁻², a maximum specific capacitance (in farad per gram, C_m) of 298 and 125 F g⁻¹ was achieved from CVs at a scan rate of 10, and 200 mV s⁻¹, respectively. The value of C_m significantly gets lower from 265 to around 95 F g⁻¹ when the deposition charge increases from 0.2 to around 6.0 C cm⁻². The long cycle-life and stability of the SnO_x coatings on graphite via the presented cathodic deposition were also demonstrated.