The Sliding Wear and Friction Behavior of M50-Graphene Self-Lubricating Composites Prepared by Laser Additive Manufacturing at Elevated Temperature
Authors:Xiyao Liu  Xiaoliang Shi  Yuchun Huang  Xiaobin Deng  Guanchen Lu  Zhao Yan  Hongyan Zhou  Bing Xue
Affiliation:1.School of Mechanical and Electronic Engineering,Wuhan University of Technology,Wuhan,China;2.College of Mechanical Engineering,Yellow River Conservancy Technical Institute,Kaifeng,China
Abstract:M50 steel is widely applied to manufacture aircraft bearings where service lives are mainly determined by the friction and wear behaviors. The main purpose of this study is to investigate the tribological behaviors and wear mechanisms of M50-1.5 wt.% graphene composites (MGC) prepared by laser additive manufacturing (LAM) (MGC-LAM) sliding against Si3N4 ball from 25 to 550 °C at 18 N–0.2 m/s. XRD, EPMA, FESEM, and EDS mapping were conducted to understand the major mechanisms leading to the improvement in the sliding behavior of MGC-LAM. The results indicated that MGC-LAM showed the excellent friction and wear performance at 25-550 °C for the lower friction coefficient of 0.16-0.52 and less wear rate of 6.1-9.5 × 10?7 mm3 N?1 m?1. Especially at 350 °C, MGC-LAM obtained the best tribological performance (0.16, 6.1 × 10?7mm3 N?1 m?1). It was attributed to the dense coral-like microstructure, as well as the formed surface lubricating structure which is composed of the upper uniform lubricating film with massive graphene and the underneath compacted layer.
Keywords:
本文献已被 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号