| X100级管线钢的组织和强韧性 |
| |
| 引用本文： | 段琳娜,刘清友,贾书君,贾成厂,谭峰亮.X100级管线钢的组织和强韧性[J].材料研究学报,2012(4):443-448. |
| |
| 作者姓名： | 段琳娜 刘清友 贾书君 贾成厂 谭峰亮 |
| |
| 作者单位： | 北京科技大学材料科学与工程学院;钢铁研究总院结构所;昆明理工大学冶金与能源工程学院 |
| |
| 摘 要： | 用光学显微镜、扫描电镜、透射电镜和EBSD等方法研究了X100管线钢热连轧钢带的微观组织、析出物、晶粒尺寸等对X100管线钢强韧性的影响。结果表明,通过合理的成分设计和TMCP工艺得到的X100管线钢的平均有效晶粒尺寸约为2.38μm,晶内含有大量位错和亚结构;显微组织由粒状贝氏体、板条贝氏体和M/A岛组成,组织中粒状贝氏体含量较多,板条贝氏体含量较少,M/A岛尺寸较小,弥散分布;细小的第二相能有效钉扎位错的移动,产生沉淀强化效果;实验钢的抗拉强度高于970 MPa,屈服强度高于800 MPa,-40℃以上的Charpy冲击功大于250 J,韧脆转变温度在-40℃与-60℃之间。
|
| 关 键 词： | 金属材料 X100管线钢 微观组织 粒状贝氏体 EBSD 强韧性 |
Microstructure Characteristics and Strength-toughness of X100 Pipeline Steel |
| |
| DUAN Linna, LIU Qingyou,JIA Shujun,JIA Chengchang,TAN Fengliang.Microstructure Characteristics and Strength-toughness of X100 Pipeline Steel[J].Chinese Journal of Materials Research,2012(4):443-448. |
| |
| Authors: | DUAN Linna LIU Qingyou JIA Shujun JIA Chengchang TAN Fengliang |
| |
| Affiliation: | (2,3) 1.School of Material Science and Engineering,University of Science and Technology Beijing,Beijing 100083 2.Institute for Structural Materials of CISRI,Beijing 100081 3.Faculty of Metallurgical and Energy Engineering,Kunming University of Science and Technology,Kunming 650093 |
| |
| Abstract: | The effects of microstructure,precipitate and grain size on strength and toughness of XlOO hot rolled strips steel were investigated by means of optical microscope,scanning electronic microscopy(SEM),transmission electron microscopy(TEM) and electron backscattered diffraction(EBSD) in this article.The results show that average effective grain size of XlOO pipeline steel with reasonable composition design reaches to 2.38μm after selected thermo-mechanical control process(TMCP),and there are a great quantity of dislocations and substructures in grains.Microstructure of XlOO strips mainly consists of granular bainite,lath bainite with plenty of fine M/A islands dispersing in the matrix or on grain boundaries.Fine precipitation particles can pin dislocation effectively,tensile strength of tested steel are higher than 970 MPa,yield strength are higher than 800 MPa,Charpy impact energy(higher than—40℃) are higher than 250 J,and ductile brittle transition temperature is between-40℃and—60℃. |
| |
| Keywords: | metallic materials X100 pipeline steel microstructure granular bainite EBSD strength and toughness |