Effects of transition metal (Ni, Mn, Cu) doping on ferroelectric properties of Bi0.9Nd0.1FeO3 thin films prepared by chemical solution deposition method

Transition metal (Ni, Mn, Cu) doped Bi_0.9Nd_0.1FeO₃ thin films were prepared on Pt(111)/Ti/SiO₂/Si(100) substrates by using a chemical solution deposition method. Compared to pure BiFeO₃ (BFO) thin film, improved ferroelectric and leakage current properties were observed in the transition metal doped thin films. The values of remnant polarization (2P _r ) and coercive electric field (2E _c ) of the transition metal doped thin films were 59 μC/cm² and 690 kV/cm at 700 kV/cm for the Ni-doped Bi_0.9Nd_0.1FeO₃ thin film, 57 μC/cm² and 523 kV/cm at 670 kV/cm for the Mn-doped thin film, and 85 μC/cm² and 729 kV/cm at 700 kV/cm for the Cu-doped thin film, respectively. The 2P _r values observed in the transition metal doped thin films were much larger than that of the BFO thin film, 21 μC/cm² at 660 kV/cm. Also the 2E _c values of in the transition metal doped thin films were lower than that of the BFO thin film, 749 kV/cm at 660 kV/cm. The reduced leakage current density was observed in the transition metal doped thin films, which is approximately two orders of magnitude lower than the BFO thin film, 2.6?×?10^?3 A/cm² at 100 kV/cm.