| 用液态含环氧基丙烯酸酯低聚物改性环氧树脂 | |
| 引用本文： | 张斌,张绪刚,张密林,孙明明,李坚辉. 用液态含环氧基丙烯酸酯低聚物改性环氧树脂[J]. 材料工程, 2007, 0(4): 3-6 |
| 作者姓名： | 张斌 张绪刚 张密林 孙明明 李坚辉 |
| 作者单位： | 1. 黑龙江省石油化学研究院,胶粘剂工程技术研究中心,哈尔滨,150040;哈尔滨工程大学,材料科学与化学工程学院,哈尔滨,150001 2. 黑龙江省石油化学研究院,胶粘剂工程技术研究中心,哈尔滨,150040 3. 哈尔滨工程大学,材料科学与化学工程学院,哈尔滨,150001 |
| 摘 要： | 采用溶液聚合法合成了以丙烯酸丁酯为主链的液态含环氧基丙烯酸酯低聚物,并用其对环氧树脂进行增韧改性.讨论甲基丙烯酸环氧丙酯以及低聚物用量对改性环氧树脂力学性能的影响,并研究了改性环氧树脂的微观形态和耐热性能.结果表明:当低聚物用量为10%(质量分数),丙烯酸丁酯和甲基丙烯酸环氧丙酯的质量比为80∶20时,改性环氧树脂的拉伸强度和冲击强度比纯环氧树脂提高6.7%和219.1%,同时体系的耐热性能基本不下降;改性环氧树脂呈两相结构,随低聚物用量增加橡胶粒子粒径尺寸增大;且Tg先升高后降低. |
| 关 键 词： | 丙烯酸丁酯 甲基丙烯酸缩水甘油酯 低聚物 改性环氧树脂 增韧 液态 环氧基 丙烯酸酯 低聚物 改性环氧树脂 Groups Epoxy Containing Oligomer Acrylate Liquid Modified 粒径尺寸 橡胶粒子 两相结构 体系 强度比 冲击 拉伸强度 质量比 |
| 文章编号： | 1001-4381(2007)04-0003-04 |
| 修稿时间： | 2006-09-29 |
Epoxy Resin Modified by Liquid Acrylate Oligomer Containing Epoxy Groups |
|
| ZHANG Bin,ZHANG Xu-gang,ZHANG Mi-lin,SUN Ming-ming,LI Jian-hui. Epoxy Resin Modified by Liquid Acrylate Oligomer Containing Epoxy Groups[J]. Journal of Materials Engineering, 2007, 0(4): 3-6 | |
| Authors: | ZHANG Bin ZHANG Xu-gang ZHANG Mi-lin SUN Ming-ming LI Jian-hui |
| Affiliation: | 1 Research Center of Adhesive Engineering Technology, Petrochemistry Institute of Heilongjiang Province, Harbin 150040, China; 2 School of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China |
| Abstract: | Liquid acrylate oligomers containing epoxy groups were synthesized by solution polymerization,and used to modify epoxy resin.The influence of epoxypropyl methacrylate(GMA) and oligomer content on the mechanical properties of modified systems was discussed.The morphology and thermodynamics properties of modified epoxy resins were studied.The results showed that the tensile strength was improved about 6.7% and impact strength was improved about 219.1%,and the property of heat resistant was remained,when mass ratio of BA/GMA was 80/20 and the mass fraction of oligomer was about 10%.The modified epoxy resins had two-phase morphology.With the increased of the oligomer content,the sizes of rubber particles increased,and Tg rised at first and then droped. |
| Keywords: | butyl acrylate epoxypropyl methacrylate oligomer modified epoxy resin tougthening |