Effect of mechanical activation on carbothermal reduction of chromite with graphite

Abstract

The carbothermal reduction of mechanically activated chromite with graphite under an argon atmosphere was investigated at temperatures between 1100 and 1400°C and the effects of the mechanical activation on chromite structure were analysed by X-ray diffraction, scanning electron microscopy and specific surface area measurement. An increase in specific surface area resulted in more contact points. The activation procedure led to amorphisation and structural disordering in chromite, and accelerated the degree of reduction and metallisation in the mixture of chromite and graphite.

On a effectué une investigation de la réduction carbothermique avec du graphite, de la chromite activée mécaniquement, en atmosphère d’argon, à des températures entre 1100 et 1400°C, et l’on a analysé les effets de l’activation mécanique sur la structure de la chromite par diffraction des rayons x, par microscopie électronique à balayage et par mesure de la surface spécifique. Une augmentation de la surface spécifique résultait en des points de contact plus nombreux. La procédure d’activation menait à une structure plus amorphe et en désordre de la chromite et accélérait le degré de réduction et de métallisation dans le mélange de chromite et de graphite.