Strengthening Characteristics of AA6111 Aluminum

Abstract

In this study the effect of cold work on the precipitation process in AA6111 was evaluated with a view to establishing its role on the strengthening characteristics. The results showed a considerable improvement in yield and tensile strength with an increasing level of prestrain. Yield and tensile strength decreased with increasing aging temperature at a given level of prestrain. At fixed levels of prestrain, the aging response varied with aging temperature. The peak aging time decreased with the increasing temperature. Scanning electron microscopy revealed the presence of intermetallics. Transmission electron microscopy showed that the density of dislocation tangles increased with an increasing degree of prestrain.

Dans cette étude, on a évalué l'effet de l'écrouissage sur le procédé de précipitation de AA6111 en vue d'établir son rôle sur les caractéristiques de renforcement. Les résultats montrent une amélioration considérable de la limite d'élasticité et de la résistance à la traction avec une augmentation du niveau de pré-déformation. La limite d'élasticité et la résistance à la traction diminuaient avec une augmentation de la température de vieillissement à un niveau donné de pré-déformation. À des nivaux fixes de pré-déformation, la réponse au vieillissement variait avec la température de vieillissement. La dureté maximale de vieillissement diminuait avec une augmentation de la température. La microscopie électronique à balayage a révélé la présence de composés intermétalliques. La microscopie électronique à transmission a montré que la densité des enchevêtrements de dislocation augmentait avec une augmentation du degré de pré-déformation.