Molybdenum steels for pipelines

Abstract

Stringent property requirements are specified for steels to be used for oil and gas pipelines, especially for application in extremely cold climates. The effect of controlled plate mill processing (including water spray cooling between hot rolling passes), and of simulated strip mill processing on the mechanical properties and microstructure of pipe skelp of varying thickness has been studied in a family of Mn-Mo-Cb steels developed to meet these specifications. By virtue of chemistry and process control, desired minimum levels of yield strength in the range of 60 to 90 ksi (415 to 620 N/mm²) have been achieved, with excellent corresponding toughness values, in strip and plate gauges up to 0.75 in (19 mm). The microstructure of these steels varies, according to chemistry, from ferrite plus pearlite to acicular ferrite.

Résumé

Des propriétés mécaniques particulièrement strictes son t exigées des aciers pour pipe-lines (gaz ou pétrole) situés spécialement dans des régions très froides. Pour une série d'aciers au Mn-Mo-Cb développés pour de telles applications, les auteurs ont étudié la variation des propriétés mécaniques et de la microstructure de tôles a tube d' épaisseur variable en fonction de la procédure de laminage contrôlé des tôles fortes (incluant un refroidissement par aspersion d'eau entre les passes) ou d'une procédure simulée de laminage des feuillards. Du fait de la composition chimique et du contrôlé du laminage, des limites d' élasticité de l'ordre de 60 à 90 ksi (415 à 620 N/mm²) ont été atteintes et sont associées a d'excellen tes valeurs de la résilience des feuillards et des tôles jusqu'à 0.75 in. (19 mm) d' épaisseur. Selon la composition, la microstructure de ces aciers varie de ferritico-perlitique à une ferrite aciculaire.