The kinetics of reaction of zinc metal with selenium vapour

Abstract

The kinetics of reaction of coupons of zinc with selenium vapour have been investigated by the thermogravimetric technique at temperatures between 350 and 415°C and at selenium pressures between 0.05 and 0.8 Torr. Cubic zinc selenide (ZnSe) was the only reaction product observed under all experimental conditions. The selenization kinetics were essentially parabolic, although at higher temperatures initially linear reactions were sometimes observed. The apparent activation energy for the selenization of zinc metal was in the range 24 to 32 kcal/mole. The selenization rate varied inversely as the square root of the selenium pressure. It is postulated that the rate-controlling step of the selenization reaction is the outward diffusion of neutral zinc interstitials through a constantly thickening zinc selenide reaction scale.

Résumé

On a étudié la cinétique de la réaction entre des plaques de zinc et la vapeur de sélénium par la méthode de thermogravimétrie dans une gamme de température et de pression de sélénium comprise entre 350 et 415°C et 0.05 et 0.8 Torr. respectivement. Le séléniure de zinc de malie cubique (ZnSe) était Ie seul produit de la réaction obtenu dans toutes les conditions expérimentales. La cinétique de séléniuration était essentiellement de forme parabolique, bien qu'on ait observé parfois aux températures plus élevées des réactions initialement linéaires. L' énergie apparente d'activation pour la séléniuration du zinc métallique était comprise dans une gamme variant entre 24 et 32 kcal/mol. La vitesse de la séléniuration était inversement proportionnelle à la racine carrée de la pression du sélénium. On suggére que l' étape déterminante de la vitesse de reaction soit la diffusion vers l'extérieuI des interstitiels de zinc électriquement neuters à travers une couche de séléniure de zinc qui s'épaissit constamment.