Internal curing by superabsorbent polymers in ultra-high performance concrete
Affiliation:1. Empa, Swiss Federal Laboratories for Materials Science and Technology, Switzerland;2. Institute of Materials and Structures, Riga Technical University, Latvia;3. Department of Building Physics and Building Materials, Lodz University of Technology, Poland;4. Institute for Building Materials (IfB), ETH Zurich, Switzerland
Abstract:To limit self-desiccation and autogenous shrinkage that may lead to early-age cracking of ultra-high performance concrete (UHPC), internal curing by means of superabsorbent polymers (SAP) may be employed. Cement pastes and UHPC with water-to-cement ratio below 0.25, with or without SAP, were studied. The absorption capacity of a solution-polymerized SAP was first determined on hardened cement pastes by SEM image analysis. It was observed that the SAP cavities become partially filled with portlandite during cement hydration. Isothermal calorimetry showed that water entrainment with SAP delays the main hydration peak, while after a couple of days it increases the degree of hydration in a manner similar to increasing the water-to-cement ratio. Internal curing by SAP is effective in reducing the internal relative humidity decrease and the autogenous shrinkage. Although the mechanical properties are affected by SAP addition, it is possible to reach compressive strengths of almost 150 MPa at 28 days.
Keywords:
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号