Modification of Sr on 4004 Aluminum Alloy |
| |
Authors: | Erjun Guo Guojian Cao Yicheng Feng Liping Wang Guojun Wang Xinyu Lv |
| |
Affiliation: | 1. School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin, 150080, People’s Republic of China 2. Northeast Light Alloy Co., Ltd, Harbin, 150060, People’s Republic of China
|
| |
Abstract: | As a brazing foil, 4004 Al alloy has good welding performance. However, the high Si content decreases the plasticity of the alloy. To improve the plasticity of 4004 Al alloy and subsequently improve the productivity of 4004 Al foil or 434 composite foil, 4004 Al alloy was modified by Al-10%Sr master alloy. Modification effects of an additional amount of Sr, modification temperature, and holding time on 4004 aluminum alloy were studied by orthogonal design. The results showed that the greatest impact parameter of 4004 aluminum alloy modification was the additional amount of Sr, followed by holding time and modification temperature. The optimum modification parameters obtained by orthogonal design were as follows: Sr addition of 0.04%, holding time of 60 min, and modification temperature of 760°C. The effect of Sr addition on modification was analyzed in detail based on orthogonal results. With increasing of Sr addition, elongation of 4004 alloy increased at first, and decreased after reaching the maximum value. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|