Surface properties and reactivity of Cu/γ-Al2O3 catalysts for NO reduction by C3H6: Influences of calcination temperatures and additives

The influences of calcination temperatures and additives for 10 wt.% Cu/γ-Al₂O₃ catalysts on the surface properties and reactivity for NO reduction by C₃H₆ in the presence of excess oxygen were investigated. The results of XRD and XPS show that the 10 wt.% Cu/γ-Al₂O₃ catalysts calcined below 973 K possess highly dispersed surface and bulk CuO phases. The 10 wt.% Cu/γ-Al₂O₃ and 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalysts calcined at 1073 K possess a CuAl₂O₄ phase with a spinel-type structure. In addition, the 10 wt.% La–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses a bulk CuO phase. The result of NO reduction by C₃H₆ shows that the CuAl₂O₄ is a more active phase than the highly dispersed and bulk CuO phase. However, the 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses significantly lower reactivity for NO reduction than the 10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K, although these catalysts possess the same CuAl₂O₄ phase. The low reactivity for NO reduction for 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K is attributed to the formation of less active CuAl₂O₄ phase with high aggregation and preferential promotion of C₃H₆ combustion to CO_x by MnO₂. The engine dynamometer test for NO reduction shows that the C₃H₆ is a more effective reducing agent for NO reduction than the C₂H₅OH. The maximum reactivity for NO reduction by C₃H₆ is reached when the NO/C₃H₆ ratio is one.