The relationship between photo-catalytic performance and optical property over Si-incorporated TiO2

This study focuses on the relationship between photo-catalytic performance and optical property over Si-incorporated TiO₂. The Si-incorporated TiO₂ particles exhibited a pure structure of anatase having a particle size of less than 20 nm and surface area of more than 190 m²/g. The absorbance did not shift to a higher wavelength in spite of the incorporation of the Si ions, but the intensity of the photoluminescence (PL) curve was the smallest in the case of the 2.0 mol% Si-TiO₂, which was related to the recombination between the excited electrons and holes. Based on these results, the photodecomposition of methyl orange in the liquid reaction was enhanced over the 2.0 mol% Si-incorporated TiO₂ compared with that over pure TiO₂: Methyl orange at 10.0 ppm was completely decomposed after 100 min when 1.0 g of the 2.0 mol% Si-incorporated TiO₂ was used.