| 旧料生产锡磷青铜带材急冷破鳞开裂原因及其探讨 |
| |
| 引用本文： | 吴子平. 旧料生产锡磷青铜带材急冷破鳞开裂原因及其探讨[J]. 有色金属材料与工程, 2006, 27(1): 10-12 |
| |
| 作者姓名： | 吴子平 |
| |
| 作者单位： | 江西理工大学,材料与化学工程学院,江西,赣州,341000 |
| |
| 摘 要： | 阐述了在实际生产过程中，因大量使用镀白旧料生产锡磷青铜带材，在急冷破鳞时易出现开裂现象及其产生的原因。根据其特有的生产工艺及特点提出了相应的解决方法。
|
| 关 键 词： | 锡磷青铜 铜板带材 镀白旧料 开裂现象 急冷破鳞 |
| 文章编号： | 1005-2046(2006)01-0010-03 |
| 收稿时间： | 2005-04-26 |
| 修稿时间： | 2005-04-26 |
Study of Cause for Fracture of Phosphor Bronze Strip Produced with Scraps during Rapid Cooling for Removing Surface Scales |
| |
| WU Zi-ping. Study of Cause for Fracture of Phosphor Bronze Strip Produced with Scraps during Rapid Cooling for Removing Surface Scales[J]. Nonferrous Metal Materials and Engineering, 2006, 27(1): 10-12 |
| |
| Authors: | WU Zi-ping |
| |
| Abstract: | The cause for the fracture of phosphor bronze strip during rapid cooling for removing the scales on its surface is studied. In view of the characteristics of the production process, a solving method for the fracture is proposed. |
| |
| Keywords: | phosphor bronze strips and plates of copper and its alloys plated scraps fracture rapidcooling tbr mmovillg scales |