A new temperature stable microwave dielectric ceramics: ZnTiNb2O8 sintered at low temperatures |
| |
Authors: | Mei GuoShuping Gong Gang DouDongxiang Zhou |
| |
Affiliation: | Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China |
| |
Abstract: | The phases, microstructure and microwave dielectric properties of ZnTiNb2O8-xTiO2 composite ceramics with different weight percentages of BaCu(B2O5) additive prepared by solid-state reaction method have been investigated using the X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). The results showed that the microwave dielectric properties were strongly dependent on densification, grain sizes and crystalline phases. The sintering temperature of ZnTiNb2O8 ceramics was reduced from 1250 °C to 950 °C by doping BaCu(B2O5) additive and the temperature coefficient of resonant frequency (τf) was adjusted from negative value of −52 ppm/°C to 0 ppm/°C by incorporating TiO2. Addition of 2 wt% BaCu(B2O5) in ZnTiNb2O8-xTiO2 (x = 0.8) ceramics sintered at 950 °C showed excellent dielectric properties of ?r = 38.89, Q × f = 14,500 GHz (f = 4.715 GHz) and τf = 0 ppm/°C, which represented very promising candidates as LTCC dielectrics for LTCC applications. |
| |
Keywords: | LTCC τf = 0 ppm/° C Microwave dielectric properties ZnTiNb2O8-xTiO2 BaCu(B2O5) |
本文献已被 ScienceDirect 等数据库收录! |
|