Synthesis and characterization of β type solid solution in the binary system of Bi2O3-Eu2O3

We have investigated Bi₂O₃-Eu₂O₃ binary system by doping with Eu₂O₃ in the composition range from 1 to 10 mole% via solid state reactions and succeeded to stabilize β-Bi₂O₃ phase which is metastable when pure. Stability of β-Bi₂O₃ polymorph was influenced by heat treatment temperature. Tetragonal type solid solution was obtained in 3–6 mole% addition range when annealed at 750°C and the range was 2–7 mole% when annealed at 800°C. We have also carried out investigations on lattice parameters, microstructural properties and elemental compositions of this β type solid solution for each doping ratio. Lattice parameters increased with amount of Eu₂O₃ addition. Our experimental observations strongly suggested that oxygen deficiency type non-stoichiometry is present in doped β type solid solutions.