Densification, microstructure, and fracture behavior of TiC/Si3N4 composites by spark plasma sintering

TiC/Si₃N₄ composites were prepared using the β-Si₃N₄ powder synthesized by self-propagating high-temperature synthesis (SHS) and 35 wt.% TiC by spark plasma sintering. Y₂O₃ and Al₂O₃ were added as sintering additives. The almost full sintered density and the highest fracture toughness (8.48 MPa·m^½) values of Si₃N₄-based ceramics could be achieved at 1550°C. No interfacial interactions were noticeable between TiC and Si₃N₄. The toughening mechanisms in TiC/Si₃N₄ composites were attributed to crack deflection, microcrack toughening, and crack impedance by the periodic compressive stress in the Si₃N₄ matrix. However, increasing microcracks easily led to excessive connection of microcracks, which would not be beneficial to the strength.