Sintering of Mixtures of Seeded Boehmite and Ultrafine α-Alumina

α-Alumina was fabricated by dry pressing mixtures of seeded boehmite and fine α-alumina (i.e., 0.2 and 0.3 μm diameter) to reduce the large shrinkage of boehmite-derived α-alumina. The maximum green density was obtained with mixtures containing ～70%α-alumina for both alumina powders. The ～15% linear shrinkage and microstructures of these samples were comparable to 100% alumina powder samples. Samples with 0.2 μm alumina sintered to densities >95% at 1300°C whereas 1400°C was needed for samples with 0.3 μm alumina. These results indicate that boehmite can be used as a substitute for relatively expensive ultrafine α-alumina powders.