Deep dephosphorization of IF steel in converter

RH oxygen top- blowing for raising temperature should be avoided to improve the cleaniness of IF steel as far as possible, which made the end point temperature of converter higher and then dephosphorization in converter became difficult. Thermodynamics and dynamics of dephosphorization process in converter were calculated to study the relationship of phosphate partition ratio to compositions of molten steel, slag, temperature in molten steel based on slag- remaining and double slag process. Through changing the first deslagging time and the composition of slag,then serial sampling from molten steel and slag in industrial production experiments, the behavior of phosphorus in molten steel was studied and then the main measures obtaining higher phosphate partition ratio in slag- remaining and double slag process are: small- sized scrap or thin steel sheet should be used to increase FeO content in slag and prevent molten steel temperature increase when oxygen blowing in converter begins. Slag with high phosphorus content should be poured when amount of oxygen blowing reachs 40% of the total; FeO content in slag should be increased to assure the mobility of slag and then reduce rephosphorization from slag to steel when amount of oxygen blowing is greater than 40% and less than 80% of the toal; the end- point slag with 4. 0 basicity and 18 mass%-20 mass% FeO content and molten steel temperature should be controlled.