Effects of MgO and MgO/Pd seed-layers on perpendicular magnetic anisotropy of CoPd thin films |
| |
Authors: | Jungho KoJangyup Son Soogil LeeSanghoon Kim Jongill Hong |
| |
Affiliation: | Department of Materials Science and Engineering, Yonsei University, Seoul, Republic of Korea |
| |
Abstract: | We studied the effects of MgO and MgO/Pd seed-layers on perpendicular magnetic anisotropy in co-sputtered CoPd films. CoPd films with the MgO seed-layer showed perpendicular magnetic properties that were superior to those with another after annealing. The loop squareness was unity, indicating strong perpendicular magnetic anisotropy, when the MgO seed-layer was thicker than 2 nm. We observed that the out-of-plane CoPd (111) texture was strongly developed, as well as the in-plane tensile stress in the CoPd films. The magnetoelastic anisotropy coming from a negative magnetostriction λ111 under the in-plane tensile stress dominating over other anisotropies is likely responsible for creating such strong perpendicular magnetic anisotropy. In the case of the MgO/Pd seed-layer, the CoPd films showed mixed anisotropy having both in-plane and out-of-plane magnetic anisotropy components after annealing. The appearance of the strong (100) texture of the CoPd films with the MgO/Pd seed-layer is believed to have caused the decrease in the perpendicular magnetic anisotropy that originated from the magnetoelastic anisotropy due to the additional contribution from the positive magnetostriction λ100 but less contribution from the negative magnetostriction λ111 when the CoPd films are under in-plane tensile stress. |
| |
Keywords: | CoPd thin films Perpendicular magnetic anisotropy Seed-layer Annealing effect |
本文献已被 ScienceDirect 等数据库收录! |