| 凝胶铸法制备牙科全瓷氧化铝及其性能 |
| |
| 引用本文： | 刘人淼,司文捷,胡楠.凝胶铸法制备牙科全瓷氧化铝及其性能[J].稀有金属材料与工程,2009,38(Z2). |
| |
| 作者姓名： | 刘人淼 司文捷 胡楠 |
| |
| 作者单位： | 清华大学新型陶瓷与精细工艺国家重点实验室,北京,100084 |
| |
| 摘 要： | 研究了氧化铝粉浆的固相含量及预烧温度、氧化铝基底块体成形工艺对用于制作全瓷冠桥的计算机辅助设计/加工(CAD/CAM) &In-Ceram玻璃渗透氧化铝陶瓷复合体性能的影响.结果表明,采用凝胶铸成形的毛坯比等静压成形的强度要高,其中固相含量55%(体积分数)、预烧温度1350 ℃、凝胶铸成形组强度较高,达到553 MPa.
|
| 关 键 词： | 玻璃渗透氧化铝陶瓷 凝胶铸成形 抗弯强度 |
Preparation and Performance of Glass-Infiltrated Ceramics by Gel-Casting |
| |
| Liu Renmiao,Si Wenjie,Hu Nan.Preparation and Performance of Glass-Infiltrated Ceramics by Gel-Casting[J].Rare Metal Materials and Engineering,2009,38(Z2). |
| |
| Authors: | Liu Renmiao Si Wenjie Hu Nan |
| |
| Affiliation: | Liu Renmiao,Si Wenjie,Hu Nan (State Key Laboratory of New Ceramics , Fine Processing,Tsinghua University,Beijing 100084,China) |
| |
| Abstract: | The fabrication process of glass infiltrated alumina ceramics (CAD/CAM&In-ceram alumina), such as solid loading, presintered temperature and forming method, was investigated. The result indicates that the bending strength of gel-casting samples is higher that that of CIP samples, and the 1350 ℃ pre-sintered gel-casting sample with 55 vol% solid loading has a bending strength as high as 553 MPa. |
| |
| Keywords: | CAD/CAM CAD/CAM glass infiltrated alumina ceramics gel-casting bending strength |