Thermally stimulated luminescence and photoluminescence investigations of Eu3+ and Eu2+ doped SrBPO5

Thermally stimulated luminescence (TSL) investigations of SrBPO₅:Eu^3?+ and SrBPO₅:Eu^2?+ phosphors were carried out in the temperature range of 300–650 K. In order to characterize the phosphors, X-ray diffraction and photoluminescence (PL) techniques were used. The emission spectrum of air heated SrBPO₅:Eu^3?+ phosphor exhibited emission bands at 590, 614, 651 and 702 nm under 248 nm excitation, assigned to transitions of Eu^3?+ ion. In phosphor prepared in reducing (Ar + 8% H₂) atmosphere, a broad emission band due to Eu^2?+ ranging from 350 to 400 nm was observed with 340 nm excitation. EPR studies have confirmed the presence of Eu^2?+ ions in the samples prepared in reducing atmosphere. TSL glow curve of SrBPO₅:Eu^3?+ had shown intense peaks around 397, 510, 547 K and a weak peak around 440 K whereas in case of SrBPO₅:Eu^2?+ system, glow peaks at 414, 478 and weak peak at 516 nm were observed. The shift in TSL glow pattern can be attributed to stabilization of different oxidation states of the dopant ion in the host lattice. Apart from this, TSL trap parameters such as trap depth and frequency factor were determined. Spectral characteristics of TSL emission have shown that Eu^3?+?/Eu^2?+ ion acts as the luminescent centre in the respective phosphors.