| 涤棉混纺织物纳米无氟拒水整理 | |
| 引用本文： | 陈镇,赵世显,黄斌,卢张延.涤棉混纺织物纳米无氟拒水整理[J].现代纺织技术,2014,22(6):18-21. |
| 作者姓名： | 陈镇 赵世显 黄斌 卢张延 |
| 作者单位： | 1. 湖南工程学院生态纺织材料及染整新技术湖南省高校重点实验室,湖南湘潭,411104 2. Nano-Tex Asia Ltd.中国香港 3. 苏州大学纺织与服装工程学院,江苏苏州,215001 |
| 基金项目： | 湖南省高校重点实验室开放基金项目 |
| 摘 要： | 采用纳米无氟拒水剂NT-X018对涤棉混纺织物进行整理,以提高其拒水性能。探讨整理液配方、工艺过程对整理后织物拒水性能、断裂强力、透气性、耐久性及手感的影响。结果表明:整理液配方为,拒水剂NT-X018 80g/L、加强剂NT-X628 30g/L、交联剂NT-504M5g/L、催化剂NT-S228 5g/L、渗透剂OS-603 1.0g/L,浴比1∶30,pH4.0左右;采用二浸二轧,预烘条件130℃×2min,焙烘条件160℃×1min,可以达到最佳的拒水整理效果,同时,整理后织物手感基本没有影响,经多次洗涤,拒水等级仍较高,说明该拒水剂的耐久性良好。 |
| 关 键 词： | 涤棉混纺织物 拒水整理 纳米无氟整理剂 |
Study on Nano Fluorine-free Water-repellent Finishing of Polyester-Cotton Fabric |
|
| CHEN Zhen,ZHAO Shixian,HUANG Bin,LU Zhangyan.Study on Nano Fluorine-free Water-repellent Finishing of Polyester-Cotton Fabric[J].Advanced Textile Technology,2014,22(6):18-21. | |
| Authors: | CHEN Zhen ZHAO Shixian HUANG Bin LU Zhangyan |
| Affiliation: | CHEN Zhen,ZHAO Shixian,HUANG Bin,LU Zhangyan(1. Key Laboratory of Ecological Textile Materials ＆ Novel Dying and Finshing Technology, Hunan Provincial Education Department, Hunan Institute of Engineering, Xiangtan 411104, China; 2. Nano-Tex Asia Ltd. , Hong kong 999077, China; 3. College of Textile ＆ Clothing Engineering, Soochow University, Suzhou 215001, China) |
| Abstract: | Nano fluorine-free water-repellent agent NT-X018 is used to finish polyester-cotton blended fabric so as to improve its water repellency.This paper discusses the influence of the formula of finishing liquor and technological process on water repellency,breaking strength,air permeability,durability and hand feeling of finished fabrics.The result shows that the formula of finishing liquor includes：water-repellent agent NT-X018 80g/L,strengthening solution NT-X628 30g/L,cross-linking agent NT-504M5g∕ L,catalyst NT-S228 5g/L,penetrant OS-603 1.0g/L,bath ratio 1∶30and pH4.0.The best water-repellent finishing effect can be achieved with two-padding two-rolling method under preliminary drying at130℃for 2min and baking at 160℃for 1min.Meanwhile,the hand feeling of the fabric is not influenced basically after finishing.Its water repellency grade is still high after washing for multiple times,indicating that this water-repellent agent has a good durability. |
| Keywords: | polyester-cotton blended fabric water-repellent finishing nano fluorine-free finishing agent |