LEACHING RATES OF ICEL-YAVCA DOLOMITE IN HYDROCHLORIC ACID SOLUTION |
| |
Authors: | Huseyin Akarsu |
| |
Affiliation: | Camis Mining Co., Is Kuleleri, Kule 3, 4 , Levent, ?stanbul, Turkey |
| |
Abstract: | Additives can give rise to obvious, step-wise changes both in the oxidation process and in the sintering process. Therefore, the oxidation and sintering characteristics measured in dried pellets prepared from pure magnetite concentrates can not be representative for those characteristics in dried pellets containing additives. The oxidation and sintering characteristics of magnetite iron ore pellets balled with a novel complex binder (namely MHA) were mainly investigated by batch isothermal oxidation measurements in this research. Combined results reveal that the thermal decomposition of MHA binder influences the oxidation and sintering processes of dried pellets. Oxidation rate of pellets increases obviously with increasing the oxidation temperature in the range from 800°C to 1000°C. And the remaining FeO content declines gradually when separately heated for 10 min at low temperature (<1000°C). However, the oxidation rate of pellets decreases distinctly when oxidation temperature is higher than 1000°C. In addition, when oxidation temperature increases from 1000°C to 1250°C, the FeO content of pellets goes up obviously, particularly at 1250°C. The FeO content in the core of sintered pellets heated at 1250°C can even reach 29.68%. SEM spectrum analysis demonstrate that some iron appears in forms of wustite in sintered pellets, which indicates that the reduction reaction of iron oxide occurs during the high temperature sintering process. This is explained by the occurrence of reducing atmospheres because of the pyrogenic decomposition of MHA binder. |
| |
Keywords: | dolomite dissolution rates dolomite leaching Icel-Yavca dolomite |
|
|