Foaming of flat glass cullet using Si3N4 and MnO2 powders
Authors:Alejandro Saburit Llaudis  María José Orts Tari  Francisco Javier García Ten  Enrico Bernardo  Paolo Colombo
Affiliation:1. Instituto de Tecnología Cerámica (ITC), Asociación de Investigación de las Industrias Cerámicas (AICE), Universitat Jaume I, Campus Universitario Riu Sec, Avda. Vicent Sos Baynat, 12006 Castellón, Spain;2. Dipartimento di Ingegneria Meccanica – Settore Materiali, Università di Padova, via Marzolo, 9, 35131 Padova, Italy;3. Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA 16802, USA
Abstract:The introduction of a compound capable of releasing oxygen, such as MnO2, greatly improves the foaming ability of Si3N4 used as foaming agent in soda-lime glass powder, leading to expansion at a relatively low temperature (800–850 °C) and short processing time (7–30 min). The effect is based on the supply of oxygen, in addition to that in the furnace atmosphere. At the highest level of porosity, however, the strength of foams is negatively affected by a coarse microstructure, determined by cell coalescence. The reduction of firing temperature or, above all, the reduction of the processing time, was found to limit the coalescence and significantly improve the strength of the foams.
Keywords:
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号