Effects of Bi0.5Na0.5HfO3 addition on the phase structure and piezoelectric properties of (K,Na)NbO3‐based ceramics

Lead‐free perovskite (1‐x)(K_0.48Na_0.48Li_0.04)Nb_0.95Sb_0.05O₃‐x(Bi_0.5Na_0.5)HfO₃ piezoelectric ceramics were prepared by a traditional ceramic fabrication method. An investigation was conducted to assess the effects of (Bi_0.5Na_0.5)HfO₃ content on the crystal structure, microstructure, phase‐transition temperatures, and piezoelectric properties of the ceramics. The X‐ray diffraction results, combined with the temperature dependence of dielectric properties, revealed that the ceramics experienced a structural transition from an orthorhombic phase to a tetragonal phase with the addition of (Bi_0.5Na_0.5)HfO₃, and a coexistence of orthorhombic and tetragonal phases was identified in the composition range of 0.005≤x≤0.015. An obviously improved piezoelectric activity was obtained for the ceramics with compositions near the orthorhombic‐tetragonal phase boundary, among which the composition x=0.005 exhibited the maximum values of piezoelectric constant d₃₃, and planar and thickness electromechanical coupling coefficients (k_p and k_t) of 246 pC/N, 0.435, and 0.554, respectively. Furthermore, the Curie temperature of the ceramics was found decreasing with the increase in (Bi_0.5Na_0.5)HfO₃ content, but still maintaining above 300°C for the phase boundary compositions. These results indicate that the ceramics are promising lead‐free candidate materials for piezoelectric applications.