植入铸造不锈钢髋关节断裂失效事例分析
引用本文:谢建辉,吴荫顺.植入铸造不锈钢髋关节断裂失效事例分析[J].上海金属,1997,19(1):29-32.
作者姓名:谢建辉  吴荫顺
作者单位:北京科技大学!100083
摘    要:利用SEM对实际使用时断裂的髋关节的断口和表面进行了分析,认为此关节的断裂为以弯曲应力为主的腐蚀疲劳断裂。疲劳裂纹首先在表面的腐蚀点孕育产生,应力和腐蚀的共同作用使得裂纹得以扩展断裂。

关 键 词:髋关节  断裂失效  腐蚀疲劳  断口  不锈钢

THE ANALYSIS OF FAILURE CAUSES FOR THE CAST STAINLESS STEEL HIP-JOINT FRACTURED IN VIVO
Xie Jianhui, Wu Yinshun, Zhu Rizhang.THE ANALYSIS OF FAILURE CAUSES FOR THE CAST STAINLESS STEEL HIP-JOINT FRACTURED IN VIVO[J].Shanghai Metals,1997,19(1):29-32.
Authors:Xie Jianhui  Wu Yinshun  Zhu Rizhang
Affiliation:University of Science & Technology Beijing
Abstract:The fracture surface of a cast stainless steel hip joint fractured in-vivo and its normal surface were studied by SEM method. It was concluded that the fracture was corrosion fatigue crack due to the bending stress. The corrosion fatigue crack which initiated from corroded place propagated and fractured because of co-effect of corrosion and stress.
Keywords:Hip Joint  Fracture Failure  Corrosion Fatigue  Fracture Surface