Effects of Al2O3 additive on sintering behavior and microwave dielectric properties of ZnTa2O6 ceramics

ZnTa₂O₆ ceramics with various amount of Al₂O₃ additive were synthesized by a conventional mixed-oxide route. The grain growth of ZnTa₂O₆ ceramics was accelerated with Al₂O₃ additive. However, excessive addition (>1.0 wt%) of Al₂O₃ leaded to abnormal grain growth. With Al₂O₃ addition, the Al₂O₃ additive did not solubilized into ZnTa₂O₆ structure but resulted in forming the second phase. The Al₂O₃ addition resulted in the lower sintering temperature of ZnTa₂O₆ ceramics and improved microwave dielectric properties. The dielectric constant (ε_r) of the samples did not change much and ranged from 32.41 to 34.33 with different amount of Al₂O₃ addition. The optimized quality factor (Q × f) was higher than 70,000 GHz as a result of the denser ceramics. The temperature coefficient of resonant frequency (τ _f ) of the doped ZnTa₂O₆ ceramics could be optimized to near-zero.