Effect of fluctuation and modification on microstructure and impact toughness of 20 wt.% Cr hypereutectic white cast iron. Einfluss durch Partikelzugaben und Modifikationen auf die Mikrostruktur und die Kerbschlagzähigkeit von übereutektischem weißen Gusseisen mit 20 Gew.‐% Cr

In the present study, Fe‐Cr‐C hypereutectic high chromium white cast iron were prepared from industry‐grade materials and subjected to the treatment of modification using Fe‐Si‐RE alloy, aluminum and a self‐made intermediate alloy, fluctuation (ferroalloy powder), and the combination of the fluctuation and the modification respectively. The structures of the treated alloy were investigated by means of the optical microscopy (OM). The impact toughness of the specimens was also examined. The fractographs of the samples were examined by scanning electron microscopy (SEM). The results showed that, with the addition of fluctuation or modifying agents, the primary carbides were refined and the impact toughness of the alloys was improved, especially with the combination of them.