Characterization and wear behavior of modified silicon nitride

Silicon nitride-based materials are applied to many tribological components because of their superior thermal and mechanical properties and corrosion resistance. The purpose of this study is to investigate the wear performance of modified silicon nitride which contained 3 wt.% La₂O₃ and 3 wt.% Y₂O₃. The relationships between microstructure and mechanical properties have been also addressed. Vickers microhardness and toughness were measured, the later being determined by means of the direct crack measurement method (DCM). Scanning electron microscopy technique (SEM) coupled with energy dispersive X-ray spectroscopy (EDS) was used for the morphological characterization of the samples as well as for the characterization of the wear scars. Wear properties were studied under a load of 10 N by using the ball-on-disk tribometer. AISI 52100 steel balls and balls of WC + 6% Co (6 mm diameter) were used as static counterparts, respectively. Steady state friction coefficients of 0.66 and 0.62 were measured for the tribological pairs WC + 6 % Co/Si₃N₄ and AISI 52100/Si₃N₄, respectively. The wear mechanism was determined in each case, and comparison between the wear performance of the traditional and modified silicon nitride is also presented.