Structure and luminescence properties of Mn-doped Zn2SiO4 prepared with extracted mesoporous silica

Zn₂SiO₄:Mn powders were prepared by solid-state reaction using extracted SBA-15 as silica source. The well crystalline willemite Zn₂SiO₄:Mn can be obtained at 800 °C, much lower than the conventional solid-state reaction temperature and lower than using the calcined SBA-15. This can be attributed to the high reactive activity of the extracted SBA-15 due to its high density silanol groups, large surface areas, and non-crystalline structure. Ultraviolet (UV) and vacuum ultraviolet (VUV) excitation spectra reveal the host lattice absorption band around 162 nm and the charge transfer transition band around 245 nm. The Zn₂SiO₄:Mn phosphor exhibits a strong green emission around 527 nm. The Zn₂SiO₄:Mn phosphor with an Mn doping concentration of 0.06, i.e., Zn_1.94Mn_0.06SiO₄, shows the highest relative emission intensity. Upon 147 nm excitation, the luminescence decay time of the green emission of Zn_1.94Mn_0.06SiO₄ around 527 nm is 8.87 ms.