The Microstructures and Mechanical Properties of V2O5-Doped Al2O3/TiAl In-Situ Composites by Reactive Hot Pressing Process

Al₂O₃/TiAl composites are successfully fabricated by the in-situ hot pressing method from the elemental powders of Ti, Al, TiO₂, and V₂O₅. The effect of V₂O₅ addition on the microstructure and mechanical properties of the Al₂O₃/TiAl in-situ composites is investigated in detail. It is found that the as-synthesized composites mainly consist of V-dissolved γ-TiAl, α₂-Ti₃Al, and Al₂O₃ particles along with a small amount of V₃Al phase, and the in-situ-formed fine Al₂O₃ particles tend to disperse on the grain boundaries of TiAl matrix. With increasing V₂O₅ content, the density and Vickers hardness of the resulting composites gradually increase, whereas the fracture toughness and flexural strength first increase and then decrease with the increase of V₂O₅ content. The composite with 3.5 wt.% V₂O₅ has the maximum value of 9.35 MPa m^1/2 and 713.36 MPa for the fracture toughness and flexural strength, respectively. The toughening mechanism is also discussed in detail.